Aspire ePTFE 膜非常適合對液體和污染物截留至關(guān)重要的應(yīng)用。
Sterlitech 的 Aspire 層壓 ePTFE 過濾器系列由發(fā)泡聚四氟乙烯制成，并以聚酯或聚丙烯為支撐。這些過濾器的微孔結(jié)構(gòu)允許氣體傳輸，同時阻擋液體、顆粒和其他污染物。
PTFE Membrane Filters, Aspire Laminated, Hydrophobic, Polypropylene Backer, 0.1-0.2 Um, 200x250mm, 5/Pk
| Product Code | Backing Layer | Pore Size (μm) | Thickness in Mil (μm) | Air Permeability (ft3/min·ft2?@ 125 Pa) | Water Entry Pressure (psi) | IPA Bubble Point (psi) | Surface Treatment |
|---|---|---|---|---|---|---|---|
| QL217 | Polypropylene | 0.1-0.2 | 6-10 (152-254) | 0.07-0.25 | >60 | >17 | Hydrophobic |
| QP952 | Polyester | 0.2 | 5-9 (127-229) | 0.15-0.35 | >50 | ≥17 | Hydrophobic |
| QP955 | Polyester | 0.2 | 5-9 (127-229) | 0.05-0.15 | >60 | >20 | Hydrophobic |
| QL231 | Polypropylene | 0.2 | 6-10 (152-254) | 0.12-0.30 | >45 | >17 | Hydrophobic |
| QL822 | Polypropylene | 0.45 | 5-9 (127-203) | 0.10-0.45 | >37 | >15 | Hydrophobic |
| QL211 | Polypropylene | 0.45 | 8-12 (203-305) | 0.6-1.2 | >21 | >10 | Hydrophobic |
| QL827 | Polypropylene | 0.45 | 4-8 (102-203) | 0.30-0.65 | >12 | N/A | Oleophobic |
| QP909 | Polyester | 1.0 | 6-10 (152-254) | 0.3-0.8 | >12 | >6 | Hydrophobic |
| QL209 | Polypropylene | 1.0 | 6-10 (152-254) | 0.6-1.2 | >18 | >5 | Hydrophobic |
| QL208 | Polypropylene | 3.0 | 6-10 (152-254) | 1.5-3.5 | >5 | >1 | Hydrophobic |
| QL207 | Polypropylene | 5.0 | 6-10 (152-254) | 3.0-5.5 | >5 | >0.5 | Hydrophobic |
| QL230 | Polypropylene | 5.0 | 6-10 (152-254) | 4.8-8.0 | >1 | >0.5 | Hydrophobic |
| QP930 | Polyester | 5.0 | 3-5 (76-127) | 3.5-7.5 | >2 | >0.6 | Hydrophobic |
2018 年 4 月，根據(jù)改進(jìn)的表征設(shè)備和程序，對單個 Aspire PTFE 膜的多項規(guī)格進(jìn)行了修訂。膜表征對膜的制造過程沒有影響，并且性能不會發(fā)生變化。
注意：
QP（聚酯）產(chǎn)品短期使用的最高工作溫度為 170°C，連續(xù)使用為 130 – 150°C。
QL（聚丙烯）產(chǎn)品短期使用的最高工作溫度為 130°C，連續(xù)使用的最高工作溫度為 80°C。
PTFE 產(chǎn)品的最高工作溫度為 260°C。
應(yīng)用：
層壓 PTFE 過濾器在用甲醇預(yù)潤濕時也可用于過濾水溶液