AQWP2是比多層消色差延遲器成本更低的替代方案。消色差四分之一波長延遲器將入射的平面偏振光轉換成與AQWP3相同的圓偏振，但是具有較小的有效帶寬。AQWP2寬帶波片很受需要小型化可穿戴產品或用于顯示系統光學隔離的微型顯示器制造商的歡迎。
AQWP2可見光消色差四分之一波長延遲器
- 有效范圍:410納米-660納米
- 最低成本的寬帶延遲器
- 真零階
- 寬接受角
- 非常大的通光孔徑
- 獨立式或層壓在玻璃之間
- 提供大孔徑，100毫米外徑
規范焦點
- . 02波浪公差
- 99%的內部透射率
AQWP2 BROADBAND QUARTERWAVE RETARDER COMPONENT
| Birefringent Material | Polymer, sandwiched between BK-7 substrates |
| Recommended Wavelength Range | λ/4, over visible region from 410 – 660nm |
| Surface Quality | 40-20 Scratch-Dig |
| Substrates | BK-7, grade-A, fine annealed |
| AR Coating | R ≤ 0.65% loss per surface (normal incidence) average, BBAR 400-900nm wavelength range |
| Size | 25.4mm outer diameter, 80% clear aperture (20mm) |
| Acceptance Angle | ± 15 degrees |
| Unit Thickness | 4.15mm +/- .20mm |
| Optic Axis Stability | ≤ 2 degree |
| Wavefront Distortion | λ/4 @ 632.8nm |
| Temperature Range | -20° C to 60° C |
| Wedge | ≤ 2 minutes |
| Damage Threshold | CW: 500 Watt/cm2 Vis Pulsed: .3 J/cm2?10 nsec pulses @ 532nm |
AQWP2 – ECONOMIC QUARTERWAVE RETARDER FILM SPECIFICATIONS
| Birefringent Material | Modified polymer |
| Polymer Index of Refraction | 1.58 |
| Polymer Thickness | .09mm, +/- 0.05mm |
| Optional AR Coating | R ≤ .75% per surface Avg., 400-700nm |
| Environmental | 60° C at 90% RH for 1000 hours 80° C for 1000 hours dry, -30° C for 1000 hours dry -20° C (1 hour) to 75° C (1 hour) for 100 cycles |
可見光寬帶四分之一波長延遲器
單層薄膜寬帶四分之一波片。AQWP2延遲器沒有表現出在單層延遲器膜中看到的顯著分散，或者遭受高的面外延遲。AQWP2是一種獨立的薄膜，但只有90微米厚。
寬帶緩速器的優勢
對OEM應用非常有用
波形因數–獨立式波片可以切片或模切，專門用于定制應用?？梢允褂脭底智懈顧C將AQWP2緩凝劑切割成幾何形狀。
費用–單位成本合同，因為原材料和勞動力較少。延遲特性與我們的標準產品完全相同。一些設計不要求低透射波前或高耐磨性。如果這是真的，自由站立聚合物消色差波片可能是一個明智的選擇。